How to heat IC in phone

[Xeno]

My Nokia phone seems to be damaged in some way. According to online forums
the solution is to heat this part of the phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do?
Wipe its memory?

 

[felix_unger]

On 07-March-2012 12:13 AM, Xeno wrote:

My Nokia phone seems to be damaged in some way. According to online forums
the solution is to heat this part of the phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do?
Wipe its memory?

go and buy a cheap unlocked phone until you can get your prob with
Telstra sorted out. Harvey Norman were advertising them for just $29!

--
rgds,

Pete
-------
“If Julia is the answer, then what was the stupid question?!”

"Julia finally got something right. Older people don't vote Labor, because they have seen too many incompetent, mismanaging, money-wasting Labor governments"

“It doesn't matter [who the leader is] the Labor Party is rotten, the policies stink, the lies insufferable, and the waste intolerable. The Muppets could do a better job!”

“All that's needed now is a small miracle to rid us of the worst prime minister and the worst government in Australia's history”

"If the WORLD as a whole cut ALL emissions tomorrow, the average temperature of the planet's not going to drop for several hundred years, perhaps over on thousand years" - Tim Flannery, Climate Commissioner

"It is a remarkable fact that despite the worldwide expenditure of perhaps US$50 billion since 1990, and the efforts of tens of thousands of scientists worldwide, no human climate signal has yet been detected that is distinct from natural variation" - Bob Carter, Research Professor of Geology, James Cook University, Townsville

"Currently, China and India combined emit 20 times as much as Australia each day, and that factor is increasing rapidly. Australia's annual savings by 2020 could be emitted by China and India within five days" - Dr. David Evans former Govt Climate Adviser.

“What I see is a country bravely beating along to the agenda of some ideological people, in this case the socialist left of the ALP and the Greens, to take away what is a natural advantage. At the end of the day, we are paying someone else to use our coal” - Peter Costello, former Federal Treasurer - http://tinyurl.com/costello-carbon-tax

“Wayne Swan threatening the Banks, is a bit like being savaged by a dead sheep!”

 

[Rob]

On 7/03/2012 11:46 AM, felix_unger wrote:

On 07-March-2012 12:13 AM, Xeno wrote:

My Nokia phone seems to be damaged in some way. According to online
forums
the solution is to heat this part of the phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do?
Wipe its memory?


go and buy a cheap unlocked phone until you can get your prob with
Telstra sorted out. Harvey Norman were advertising them for just $29!

Yep

to the op have you thought of a hair dryer?

 

[Bob Milutinovic]

"Xeno" <xeno@no.spam.no> wrote in message
news:jj52gu$4tc$1@speranza.aioe.org...

My Nokia phone seems to be damaged in some way. According to online
forums the solution is to heat this part of the phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do?
Wipe its memory?

http://jaycar.com.au/productView.asp?ID=TH1602

But I'd be VERY cautious about accepting advice from posters on an anonymous
forum.

By the looks of it, you suspect there's a fault caused by improper soldering
on a particular component in your 'phone, and someone's suggested you should
apply heat in an attempt to re-flow the solder to re-make the connection.
Though this does have merit, the method by which they've suggested you do it
will more likely lead to more problems rather than less.

Consider this: the temperature which the solder will need to get to to
re-flow, is greater than both the operating and storage temperatures of the
IC you're trying to re-connect. What do you think will happen?

--
Bob Milutinovic
Cognicom

 

[Rod Speed]

Bob Milutinovic wrote

Xeno <xeno@no.spam.no> wrote

My Nokia phone seems to be damaged in some way. According to online forums the solution is to heat this part of the
phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do? Wipe its memory?

http://jaycar.com.au/productView.asp?ID=TH1602

But I'd be VERY cautious about accepting advice from posters on an anonymous forum.

By the looks of it, you suspect there's a fault caused by improper
soldering on a particular component in your 'phone, and someone's
suggested you should apply heat in an attempt to re-flow the solder
to re-make the connection. Though this does have merit, the method by which they've suggested you do it will more
likely lead to more
problems rather than less.

Consider this: the temperature which the solder will need to get to to
re-flow, is greater than both the operating and storage temperatures
of the IC you're trying to re-connect. What do you think will happen?

And if the phone really does have that fault, it was never a good of
merchantable quality and he is legally entitled to either a full replacement
or his money back and that is his choice, not Telstra's as well.

Corse he doesnt get the money back for the calls he made.

 

[Xeno]

"Rod Speed" <rod.speed.aaa@gmail.com> wrote in message
news:9rodbtFe7iU1@mid.individual.net...

Bob Milutinovic wrote
Xeno <xeno@no.spam.no> wrote

My Nokia phone seems to be damaged in some way. According to online
forums the solution is to heat this part of the phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it
do? Wipe its memory?

http://jaycar.com.au/productView.asp?ID=TH1602

But I'd be VERY cautious about accepting advice from posters on an
anonymous forum.

By the looks of it, you suspect there's a fault caused by improper
soldering on a particular component in your 'phone, and someone's
suggested you should apply heat in an attempt to re-flow the solder
to re-make the connection. Though this does have merit, the method by
which they've suggested you do it will more likely lead to more
problems rather than less.

Consider this: the temperature which the solder will need to get to to
re-flow, is greater than both the operating and storage temperatures
of the IC you're trying to re-connect. What do you think will happen?

And if the phone really does have that fault, it was never a good of
merchantable quality and he is legally entitled to either a full
replacement
or his money back and that is his choice, not Telstra's as well.

Corse he doesnt get the money back for the calls he made.

Unfortunately I have agreed over the phone to allow them to resolve the
issue by waiving the cancellation fee. I have probably lost my chance of
pursuing them further.

 

[Rob]

On 7/03/2012 5:26 PM, Rod Speed wrote:

Bob Milutinovic wrote
Xeno<xeno@no.spam.no> wrote

My Nokia phone seems to be damaged in some way. According to online forums the solution is to heat this part of the
phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do? Wipe its memory?

http://jaycar.com.au/productView.asp?ID=TH1602

But I'd be VERY cautious about accepting advice from posters on an anonymous forum.

By the looks of it, you suspect there's a fault caused by improper
soldering on a particular component in your 'phone, and someone's
suggested you should apply heat in an attempt to re-flow the solder
to re-make the connection. Though this does have merit, the method by which they've suggested you do it will more
likely lead to more
problems rather than less.

Consider this: the temperature which the solder will need to get to to
re-flow, is greater than both the operating and storage temperatures
of the IC you're trying to re-connect. What do you think will happen?

And if the phone really does have that fault, it was never a good of
merchantable quality and he is legally entitled to either a full replacement
or his money back and that is his choice, not Telstra's as well.

Corse he doesnt get the money back for the calls he made.

Plus if decides to play with heating the board, could invalidate the
warranty due to heat damage.

 

[Rod Speed]

Rob wrote

Rod Speed wrote
Bob Milutinovic wrote
Xeno<xeno@no.spam.no> wrote

My Nokia phone seems to be damaged in some way. According to online forums the solution is to heat this part of
the phone:

http://img72.imageshack.us/img72/8467/icheat.jpg

How do you go about 'heating' this component? What would heating it do? Wipe its memory?

http://jaycar.com.au/productView.asp?ID=TH1602

But I'd be VERY cautious about accepting advice from posters on an anonymous forum.

By the looks of it, you suspect there's a fault caused by improper
soldering on a particular component in your 'phone, and someone's
suggested you should apply heat in an attempt to re-flow the solder
to re-make the connection. Though this does have merit, the method
by which they've suggested you do it will more likely lead to more
problems rather than less.

Consider this: the temperature which the solder will need to get to to re-flow, is greater than both the operating
and storage temperatures
of the IC you're trying to re-connect. What do you think will happen?

And if the phone really does have that fault, it was never a good of
merchantable quality and he is legally entitled to either a full replacement or his money back and that is his
choice, not Telstra's as well.

Corse he doesnt get the money back for the calls he made.

Plus if decides to play with heating the board, could invalidate the warranty due to heat damage.

Absolutely guaranteed to do that in fact.

Corse they may not even bother to check inside etc.